Chromium

Chromium
24Cr
- ↑ Cr ↓ Mo Periodic table vanadium ← chromium → manganese
Appearance
silvery metallic
General properties
Name, symbol, number	chromium, Cr, 24
Pronunciation	/ ˈ k r oʊ m i ə m / KROH-mee-əm
Metallic category	transition metal
Group, period, block	6, 4, d
Standard atomic weight	51.9961(6)
Electron configuration	[Ar] 3d5 4s1 2, 8, 13, 1
History
Discovery	Louis Nicolas Vauquelin (1797)
First isolation	Louis Nicolas Vauquelin (1798)
Physical properties
Phase	solid
Density (near r.t.)	7.19 g·cm−3
Liquid density at m.p.	6.3 g·cm−3
Melting point	2180 K, 1907 °C, 3465 °F
Boiling point	2944 K, 2671 °C, 4840 °F
Heat of fusion	21.0 kJ·mol−1
Heat of vaporization	339.5 kJ·mol−1
Molar heat capacity	23.35 J·mol−1·K−1
Vapor pressure
P (Pa) 1 10 100 1 k 10 k 100 k at T (K) 1656 1807 1991 2223 2530 2942
Atomic properties
Oxidation states	6, 5, 4, 3, 2, 1, -1, -2 (strongly acidic oxide)
Electronegativity	1.66 (Pauling scale)
Ionization energies ( more)	1st: 652.9 kJ·mol−1
	2nd: 1590.6 kJ·mol−1
	3rd: 2987 kJ·mol−1
Atomic radius	128 pm
Covalent radius	139±5 pm
Miscellanea
Crystal structure	body-centered cubic
Magnetic ordering	AFM (rather: SDW)
Electrical resistivity	(20 °C) 125 nΩ·m
Thermal conductivity	93.9 W·m−1·K−1
Thermal expansion	(25 °C) 4.9 µm·m−1·K−1
Speed of sound (thin rod)	(20 °C) 5940 m·s−1
Young's modulus	279 GPa
Shear modulus	115 GPa
Bulk modulus	160 GPa
Poisson ratio	0.21
Mohs hardness	8.5
Vickers hardness	1060 MPa
Brinell hardness	1120 MPa
CAS registry number	7440-47-3
Most stable isotopes
Main article: Isotopes of chromium
iso NA half-life DM DE ( MeV) DP 50Cr 4.345% >1.3×1018 y β+β+ 1.167 50Ti 51Cr syn 27.7025 d ε - 51V γ 0.320 - 52Cr 83.789% 52Cr is stable with 28 neutrons 53Cr 9.501% 53Cr is stable with 29 neutrons 54Cr 2.365% 54Cr is stable with 30 neutrons

Chromium is a chemical element which has the symbol Cr and atomic number 24. It is the first element in Group 6. It is a steely-gray, lustrous, hard metal that takes a high polish and has a high melting point. It is also odorless, tasteless, and malleable. The name of the element is derived from the Greek word "chrōma" (χρώμα), meaning colour, because many of its compounds are intensely coloured.

Chromium oxide was used by the Chinese in the Qin dynasty over 2,000 years ago to coat metal weapons found with the Terracotta Army. Chromium was discovered as an element after it came to the attention of the western world in the red crystalline mineral crocoite ( lead(II) chromate), discovered in 1761 and initially used as a pigment. Louis Nicolas Vauquelin first isolated chromium metal from this mineral in 1797. Since Vauquelin's first production of metallic chromium, small amounts of native (free) chromium metal have been discovered in rare minerals, but these are not used commercially. Instead, nearly all chromium is commercially extracted from the single commercially viable ore chromite, which is iron chromium oxide (FeCr₂O₄). Chromite is also now the chief source of chromium for chromium pigments.

Chromium metal and ferrochromium alloy are commercially produced from chromite by silicothermic or aluminothermic reactions, or by roasting and leaching processes. Chromium metal has proven of high value due to its high corrosion resistance and hardness. A major development was the discovery that steel could be made highly resistant to corrosion and discoloration by adding metallic chromium to form stainless steel. This application, along with chrome plating ( electroplating with chromium) currently comprise 85% of the commercial use for the element, with applications for chromium compounds forming the remainder.

Trivalent chromium (Cr(III)) ion is possibly required in trace amounts for sugar and lipid metabolism, although the issue remains in debate. In larger amounts and in different forms, chromium can be toxic and carcinogenic. The most prominent example of toxic chromium is hexavalent chromium (Cr(VI)). Abandoned chromium production sites often require environmental cleanup.

Characteristics

Physical

Chromium is remarkable for its magnetic properties: it is the only elemental solid which shows antiferromagnetic ordering at room temperature (and below). Above 38 °C, it transforms into a paramagnetic state.

Passivation

Chromium metal left standing in air is passivated by oxygen, forming a thin protective oxide surface layer. This layer is a spinel structure only a few atoms thick. It is very dense, and prevents the diffusion of oxygen into the underlying material. This barrier is in contrast to iron or plain carbon steels, where the oxygen migrates into the underlying material and causes rusting. The passivation can be enhanced by short contact with oxidizing acids like nitric acid. Passivated chromium is stable against acids. The opposite effect can be achieved by treatment with a strong reducing agent that destroys the protective oxide layer on the metal. Chromium metal treated in this way readily dissolves in weak acids.

Chromium, unlike metals such as iron and nickel, does not suffer from hydrogen embrittlement. However, it does suffer from nitrogen embrittlement, reacting with nitrogen from air and forming brittle nitrides at the high temperatures necessary to work the metal parts.

Occurrence

Chromium is the 24th most abundant element in Earth's crust with an average concentration of 100 ppm. Chromium compounds are found in the environment, due to erosion of chromium-containing rocks and can be distributed by volcanic eruptions. The concentrations range in soil is between 1 and 3000 mg/kg, in sea water 5 to 800 µg/liter, and in rivers and lakes 26 µg/liter to 5.2 mg/liter. Chromium is mined as chromite (FeCr₂O₄) ore. About two-fifths of the chromite ores and concentrates in the world are produced in South Africa, while Kazakhstan, India, Russia, and Turkey are also substantial producers. Untapped chromite deposits are plentiful, but geographically concentrated in Kazakhstan and southern Africa.

Although rare, deposits of native chromium exist. The Udachnaya Pipe in Russia produces samples of the native metal. This mine is a kimberlite pipe, rich in diamonds, and the reducing environment helped produce both elemental chromium and diamond.

The relation between Cr(III) and Cr(VI) strongly depends on pH and oxidative properties of the location, but in most cases, the Cr(III) is the dominating species, although in some areas the ground water can contain up to 39 µg/liter of total chromium of which 30 µg/liter is present as Cr(VI).

Isotopes

Naturally occurring chromium is composed of three stable isotopes; ⁵²Cr, ⁵³Cr and ⁵⁴Cr with ⁵²Cr being the most abundant (83.789% natural abundance). 19 radioisotopes have been characterized with the most stable being ⁵⁰Cr with a half-life of (more than) 1.8×10¹⁷ years, and ⁵¹Cr with a half-life of 27.7 days. All of the remaining radioactive isotopes have half-lives that are less than 24 hours and the majority of these have half-lives that are less than 1 minute. This element also has 2 meta states.

⁵³Cr is the radiogenic decay product of ⁵³Mn. Chromium isotopic contents are typically combined with manganese isotopic contents and have found application in isotope geology. Mn-Cr isotope ratios reinforce the evidence from ²⁶Al and ¹⁰⁷Pd for the early history of the solar system. Variations in ⁵³Cr/⁵²Cr and Mn/Cr ratios from several meteorites indicate an initial ⁵³Mn/⁵⁵Mn ratio that suggests Mn-Cr isotopic composition must result from in-situ decay of ⁵³Mn in differentiated planetary bodies. Hence ⁵³Cr provides additional evidence for nucleosynthetic processes immediately before coalescence of the solar system.

The isotopes of chromium range in atomic mass from 43  u (⁴³Cr) to 67 u (⁶⁷Cr). The primary decay mode before the most abundant stable isotope, ⁵²Cr, is electron capture and the primary mode after is beta decay. ⁵³Cr has been posited as a proxy for atmospheric oxygen concentration.

Compounds

Oxidation states
−2	Na2[Cr(CO)5]
−1	Na2[Cr2(CO)10]
0	Cr(C6H6)2
+1	K3[Cr(CN)5NO]
+2	CrCl2
+3	CrCl3
+4	K2CrF6
+5	K3CrO8
+6	K2CrO4

Chromium is a member of the transition metals, in group 6. Chromium(0) has an electronic configuration of 4s¹3d⁵, owing to the lower energy of the high spin configuration. Chromium exhibits a wide range of possible oxidation states, where the +3 state is most stable energetically; the +3 and +6 states are most commonly observed in chromium compounds, whereas the +1, +4 and +5 states are rare.

The following is the Pourbaix diagram for chromium in pure water, perchloric acid or sodium hydroxide:

Chromium(III)

A large number of chromium(III) compounds are known. Chromium(III) can be obtained by dissolving elemental chromium in acids like hydrochloric acid or sulfuric acid. The Cr³⁺ ion has a similar radius (63  pm) to the Al³⁺ ion (radius 50 pm), so they can replace each other in some compounds, such as in chrome alum and alum. When a trace amount of Cr³⁺ replaces Al³⁺ in corundum (aluminium oxide, Al₂O₃), the red-colored ruby is formed.

Chromium(III) ions tend to form octahedral complexes. The colors of these complexes is determined by the ligands attached to the Cr centre. The commercially available chromium(III) chloride hydrate is the dark green complex [CrCl₂(H₂O)₄]Cl. Closely related compounds have different colours: pale green [CrCl(H₂O)₅]Cl₂ and the violet [Cr(H₂O)₆]Cl₃. If water-free green chromium(III) chloride is dissolved in water then the green solution turns violet after some time, due to the substitution of water by chloride in the inner coordination sphere. This kind of reaction is also observed with solutions of chrome alum and other water-soluble chromium(III) salts.

Chromium(III) hydroxide (Cr(OH)₃) is amphoteric, dissolving in acidic solutions to form [Cr(H₂O)₆]³⁺, and in basic solutions to form [Cr(OH)₆]³⁻. It is dehydrated by heating to form the green chromium(III) oxide (Cr₂O₃), which is the stable oxide with a crystal structure identical to that of corundum.

Chromium(VI)

Chromium(VI) compounds are powerful oxidants at low or neutral pH. Most important are chromate anion (CrO2−
4) and dichromate (Cr₂O₇^2-) anions, which exist in equilibrium:

2 [CrO₄]^2- + 2 H⁺ [Cr₂O₇]^2- + H₂O

Chromium(VI) halides are known also and include the hexafluoride CrF₆ and chromyl chloride (CrO₂Cl₂).

Sodium chromate is produced industrially by the oxidative roasting of chromite ore with calcium or sodium carbonate. The dominant species is therefore, by the law of mass action, determined by the pH of the solution. The change in equilibrium is visible by a change from yellow (chromate) to orange ( dichromate), such as when an acid is added to a neutral solution of potassium chromate. At yet lower pH values, further condensation to more complex oxyanions of chromium is possible.

Both the chromate and dichromate anions are strong oxidizing reagents at low pH:

Cr₂O2−
7 + 14 H₃O⁺ + 6 e⁻ → 2 Cr³⁺ + 21 H₂O (ε₀ = 1.33 V)

They are, however, only moderately oxidizing at high pH:

CrO2−
4 + 4 H₂O + 3 e⁻ → Cr(OH)₃ + 5 OH⁻ (ε₀ = −0.13 V)

Chromium(VI) compounds in solution can be detected by adding an acidic hydrogen peroxide solution. The unstable dark blue chromium(VI) peroxide (CrO₅) is formed, which can be stabilized as an ether adduct CrO₅·OR₂.

Chromic acid has the hypothetical formula H₂CrO₄. It is a vaguely described chemical, despite many well-defined chromates and dichromates are known. The dark red chromium(VI) oxide CrO₃, the acid anhydride of chromic acid, is sold industrially as "chromic acid". It can be produced by mixing sulfuric acid with dichromate, and is a strong oxidizing agent.

Chromium(V) and chromium(IV)

The oxidation state +5 is only realized in few compounds but are intermediates in many reactions involving oxidations by chromate. The only binary compound is the volatile chromium(V) fluoride (CrF₅). This red solid has a melting point of 30 °C and a boiling point of 117 °C. It can be synthesized by treating chromium metal with fluorine at 400 °C and 200 bar pressure. The peroxochromate(V) is another example of the +5 oxidation state. Potassium peroxochromate (K₃[Cr(O₂)₄]) is made by reacting potassium chromate with hydrogen peroxide at low temperatures. This red brown compound is stable at room temperature but decomposes spontaneously at 150–170 °C.

Compounds of chromium(IV) (in the +4 oxidation state) are slightly more common than those of chromium(V). The tetrahalides, CrF₄, CrCl₄, and CrBr₄, can be produced by treating the trihalides (CrX₃) with the corresponding halogen at elevated temperatures. Such compounds are susceptible to disproportionation reactions and are not stable in water.

Chromium(II)

Many chromium(II) compounds are known, including the water-stable chromium(II) chloride, CrCl₂, which can be made by reduction of chromium(III) chloride with zinc. The resulting bright blue solution is only stable at neutral pH. Many chromous carboxylates are also known, most famously, the red chromous acetate (Cr₂(O₂CCH₃)₄), which features a quadruple bond.

Chromium(I)

Most Cr(I) compounds are obtained by oxidation of electron-rich, octahedral Cr(0) complexes. Other Cr(I) complexes contain cyclopentadienyl ligands. As verified by X-ray diffraction, a Cr-Cr quintuple bond (length 183.51(4)  pm) has also been described. Extremely bulky monodentate ligands stabilize this compound by shielding the quintuple bond from further reactions.

Chromium(0)

Many chromium(0) compounds are known. Most are derivatives of chromium hexacarbonyl or bis(benzene)chromium.

History

Weapons found in burial pits dating from the late 3rd century B.C. Qin Dynasty of the Terracotta Army near Xi'an, China have been analyzed by archaeologists. Although buried more than 2,000 years ago, the ancient bronze tips of crossbow bolts and swords found at the site showed unexpectedly little corrosion, possibly because the bronze was deliberately coated with a thin layer of chromium oxide. However, this oxide layer was not chromium metal or chrome plating as we know it.

Chromium minerals as pigments came to the attention of the west in the 18th century. On 26 July 1761, Johann Gottlob Lehmann found an orange-red mineral in the Beryozovskoye mines in the Ural Mountains which he named Siberian red lead. Though misidentified as a lead compound with selenium and iron components, the mineral was in fact crocoite ( lead chromate) with a formula of PbCrO₄.

In 1770, Peter Simon Pallas visited the same site as Lehmann and found a red lead mineral that had useful properties as a pigment in paints. The use of Siberian red lead as a paint pigment then developed rapidly. A bright yellow pigment made from crocoite also became fashionable.

In 1797, Louis Nicolas Vauquelin received samples of crocoite ore. He produced chromium trioxide (CrO₃) by mixing crocoite with hydrochloric acid. In 1798, Vauquelin discovered that he could isolate metallic chromium by heating the oxide in a charcoal oven, making him the discoverer of the element. Vauquelin was also able to detect traces of chromium in precious gemstones, such as ruby or emerald.

During the 1800s, chromium was primarily used as a component of paints and in tanning salts. At first, crocoite from Russia was the main source, but in 1827, a larger chromite deposit was discovered near Baltimore, United States. This made the United States the largest producer of chromium products till 1848 when large deposits of chromite were found near Bursa, Turkey.

Chromium is also known for its luster when polished. It is used as a protective and decorative coating on car parts, plumbing fixtures, furniture parts and many other items, usually applied by electroplating. Chromium was used for electroplating as early as 1848, but this use only became widespread with the development of an improved process in 1924.

Metal alloys now account for 85% of the use of chromium. The remainder is used in the chemical industry and refractory and foundry industries.

Production

Approximately 4.4 million metric tons of marketable chromite ore were produced in 2000, and converted into ~3.3 million tons of ferro-chrome with an approximate market value of 2.5 billion United States dollars. The largest producers of chromium ore have been South Africa (44%) India (18%), Kazakhstan (16%) Zimbabwe (5%), Finland (4%) Iran (4%) and Brazil (2%) with several other countries producing the rest of less than 10% of the world production.

The two main products of chromium ore refining are ferrochromium and metallic chromium. For those products the ore smelter process differs considerably. For the production of ferrochromium, the chromite ore (FeCr₂O₄) is reduced in large scale in electric arc furnace or in smaller smelters with either aluminium or silicon in an aluminothermic reaction.

For the production of pure chromium, the iron has to be separated from the chromium in a two step roasting and leaching process. The chromite ore is heated with a mixture of calcium carbonate and sodium carbonate in the presence of air. The chromium is oxidized to the hexavalent form, while the iron forms the stable Fe₂O₃. The subsequent leaching at higher elevated temperatures dissolves the chromates and leaves the insoluble iron oxide. The chromate is converted by sulfuric acid into the dichromate.

4 FeCr₂O₄ + 8 Na₂CO₃ + 7 O₂ → 8 Na₂CrO₄ + 2 Fe₂O₃ + 8 CO₂

2 Na₂CrO₄ + H₂SO₄ → Na₂Cr₂O₇ + Na₂SO₄ + H₂O

The dichromate is converted to the chromium(III) oxide by reduction with carbon and then reduced in an aluminothermic reaction to chromium.

Na₂Cr₂O₇ + 2 C → Cr₂O₃ + Na₂CO₃ + CO

Cr₂O₃ + 2 Al → Al₂O₃ + 2 Cr

Applications

Metallurgy

The strengthening effect of forming stable metal carbides at the grain boundaries and the strong increase in corrosion resistance made chromium an important alloying material for steel. The high-speed tool steels contain between 3 and 5% chromium. Stainless steel, the main corrosion-proof metal alloy, is formed when chromium is added to iron in sufficient concentrations, usually above 11%. For its formation, ferrochromium is added to the molten iron. Also nickel-based alloys increase in strength due to the formation of discrete, stable metal carbide particles at the grain boundaries. For example, Inconel 718 contains 18.6% chromium. Because of the excellent high-temperature properties of these nickel superalloys, they are used in jet engines and gas turbines in lieu of common structural materials.

The relative high hardness and corrosion resistance of unalloyed chromium makes it a good surface coating, being still the most "popular" metal coating with unparalleled combined durability. A thin layer of chromium is deposited on pretreated metallic surfaces by electroplating techniques. There are two deposition methods: Thin, below 1 µm thickness, layers are deposited by chrome plating, and are used for decorative surfaces. If wear-resistant surfaces are needed then thicker chromium layers are deposited. Both methods normally use acidic chromate or dichromate solutions. To prevent the energy-consuming change in oxidation state, the use of chromium(III) sulfate is under development, but for most applications, the established process is used.

In the chromate conversion coating process, the strong oxidative properties of chromates are used to deposit a protective oxide layer on metals like aluminium, zinc and cadmium. This passivation and the self-healing properties by the chromate stored in the chromate conversion coating, which is able to migrate to local defects, are the benefits of this coating method. Because of environmental and health regulations on chromates, alternative coating method are under development.

Anodizing of aluminium is another electrochemical process, which does not lead to the deposition of chromium, but uses chromic acid as electrolyte in the solution. During anodization, an oxide layer is formed on the aluminium. The use of chromic acid, instead of the normally used sulfuric acid, leads to a slight difference of these oxide layers. The high toxicity of Cr(VI) compounds, used in the established chromium electroplating process, and the strengthening of safety and environmental regulations demand a search for substitutes for chromium or at least a change to less toxic chromium(III) compounds.

Dye and pigment

The mineral crocoite ( lead chromate PbCrO₄) was used as a yellow pigment shortly after its discovery. After a synthesis method became available starting from the more abundant chromite, chrome yellow was, together with cadmium yellow, one of the most used yellow pigments. The pigment does not photodegrade, but it tends to darken due to the formation of chromium(III) oxide. It has a strong colour, and was used for school buses in the US and for Postal Service (for example Deutsche Post) in Europe. The use of chrome yellow declined due to environmental and safety concerns and was replaced by organic pigments or alternatives free from lead and chromium. Other pigments based on chromium are, for example, the bright red pigment chrome red, which is a basic lead chromate (PbCrO₄·Pb(OH)₂). A very important chromate pigment, which was used widely in metal primer formulations, was zinc chromate, now replaced by zinc phosphate. A wash primer was formulated to replace the dangerous practice of pretreating aluminium aircraft bodies with a phosphoric acid solution. This used zinc tetroxychromate dispersed in a solution of polyvinyl butyral. An 8% solution of phosphoric acid in solvent was added just before application. It was found that an easily oxidized alcohol was an essential ingredient. A thin layer of about 10–15 µm was applied, which turned from yellow to dark green when it was cured. There is still a question as to the correct mechanism. Chrome green is a mixture of Prussian blue and chrome yellow, while the chrome oxide green is chromium(III) oxide.

Chromium oxides are also used as a green colour in glassmaking and as a glaze in ceramics. Green chromium oxide is extremely light-fast and as such is used in cladding coatings. It is also the main ingredient in IR reflecting paints, used by the armed forces, to paint vehicles, to give them the same IR reflectance as green leaves.

Synthetic ruby and the first laser

Natural rubies are corundum (aluminium oxide) crystals that are colored red (the rarest type) due to chromium (III) ions (other colors of corundum gems are termed sapphires). A red-colored artificial ruby may also be achieved by doping chromium(III) into artificial corundum crystals, thus making chromium a requirement for making synthetic rubies. Such a synthetic ruby crystal was the basis for the first laser, produced in 1960, which relied on stimulated emission of light from the chromium atoms in such a crystal.

Wood preservative

Because of their toxicity, chromium(VI) salts are used for the preservation of wood. For example, chromated copper arsenate (CCA) is used in timber treatment to protect wood from decay fungi, wood attacking insects, including termites, and marine borers. The formulations contain chromium based on the oxide CrO₃ between 35.3% and 65.5%. In the United States, 65,300 metric tons of CCA solution have been used in 1996.

Tanning

Chromium(III) salts, especially chrome alum and chromium(III) sulfate, are used in the tanning of leather. The chromium(III) stabilizes the leather by cross linking the collagen fibers. Chromium tanned leather can contain between 4 and 5% of chromium, which is tightly bound to the proteins. Although the form of chromium used for tanning is not the toxic hexavalent variety, there remains interest in management of chromium in the tanning industry such as recovery and reuse, direct/indirect recycling, use of less chromium or "chrome-less" tanning are practiced to better manage chromium in tanning.

Refractory material

The high heat resistivity and high melting point makes chromite and chromium(III) oxide a material for high temperature refractory applications, like blast furnaces, cement kilns, molds for the firing of bricks and as foundry sands for the casting of metals. In these applications, the refractory materials are made from mixtures of chromite and magnesite. The use is declining because of the environmental regulations due to the possibility of the formation of chromium(VI).

Catalysts

Several chromium compounds are used as catalysts for processing hydrocarbons. For example the Phillips catalysts for the production of polyethylene are mixtures of chromium and silicon dioxide or mixtures of chromium and titanium and aluminium oxide. Fe-Cr mixed oxides are employed as high-temperature catalysts for the water gas shift reaction. Copper chromite is a useful hydrogenation catalyst.

Other use

• Chromium(IV) oxide (CrO₂) is a magnetic compound. Its ideal shape anisotropy, which imparts high coercivity and remnant magnetization, made it a compound superior to the γ-Fe₂O₃. Chromium(IV) oxide is used to manufacture magnetic tape used in high-performance audio tape and standard audio cassettes. Chromates can prevent corrosion of steel under wet conditions, and therefore chromates are added to drilling muds.
• Chromium(III) oxide is a metal polish known as green rouge.
• Chromic acid is a powerful oxidizing agent and is a useful compound for cleaning laboratory glassware of any trace of organic compounds. It is prepared in situ by dissolving potassium dichromate in concentrated sulfuric acid, which is then used to wash the apparatus. Sodium dichromate is sometimes used because of its higher solubility (50 g/L versus 200 g/L respectively). Potassium dichromate is a chemical reagent, used in cleaning laboratory glassware and as a titrating agent. It is also used as a mordant (i.e., a fixing agent) for dyes in fabric.

Biological role

Trivalent chromium (Cr(III) or Cr³⁺) occurs in trace amounts in foods and waters, and appears to be benign. In contrast, hexavalent chromium (Cr(VI) or Cr⁶⁺) is very toxic and mutagenic when inhaled. Cr(VI) has not been established as a carcinogen when in solution, although it may cause allergic contact dermatitis (ACD).

Chromium deficiency, involving a lack of Cr(III) in the body, or perhaps some complex of it, such as glucose tolerance factor is controversial, or is at least extremely rare. Chromium has no verified biological role and has been classified by some as not essential for mammals. However, other reviews have regarded it as an essential trace element in humans.

Chromium deficiency has been attributed to only three people on long-term parenteral nutrition, which is when a patient is fed a liquid diet through intravenous drips for long periods of time.

Although no biological role for chromium has ever been demonstrated, dietary supplements for chromium include chromium(III) picolinate, chromium(III) polynicotinate, and related materials. The benefit of those supplements is questioned by some studies. The use of chromium-containing dietary supplements is controversial, owing to the absence of any verified biological role, the expense of these supplements, and the complex effects of their use. The popular dietary supplement chromium picolinate complex generates chromosome damage in hamster cells (due to the picolinate ligand). In the United States the dietary guidelines for daily chromium uptake were lowered in 2001 from 50–200 µg for an adult to 35 µg (adult male) and to 25 µg (adult female).

Precautions

Water insoluble chromium(III) compounds and chromium metal are not considered a health hazard, while the toxicity and carcinogenic properties of chromium(VI) have been known for a long time. Because of the specific transport mechanisms, only limited amounts of chromium(III) enter the cells. Several in vitro studies indicated that high concentrations of chromium(III) in the cell can lead to DNA damage. Acute oral toxicity ranges between 1.5 and 3.3 mg/kg. The proposed beneficial effects of chromium(III) and the use as dietary supplements yielded some controversial results, but recent reviews suggest that moderate uptake of chromium(III) through dietary supplements poses no risk.

Cr(VI)

The acute oral toxicity for chromium(VI) ranges between 50 and 150 µg/kg. In the body, chromium(VI) is reduced by several mechanisms to chromium(III) already in the blood before it enters the cells. The chromium(III) is excreted from the body, whereas the chromate ion is transferred into the cell by a transport mechanism, by which also sulfate and phosphate ions enter the cell. The acute toxicity of chromium(VI) is due to its strong oxidational properties. After it reaches the blood stream, it damages the kidneys, the liver and blood cells through oxidation reactions. Hemolysis, renal and liver failure are the results of these damages. Aggressive dialysis can improve the situation.

The carcinogenity of chromate dust is known for a long time, and in 1890 the first publication described the elevated cancer risk of workers in a chromate dye company. Three mechanisms have been proposed to describe the genotoxicity of chromium(VI). The first mechanism includes highly reactive hydroxyl radicals and other reactive radicals which are by products of the reduction of chromium(VI) to chromium(III). The second process includes the direct binding of chromium(V), produced by reduction in the cell, and chromium(IV) compounds to the DNA. The last mechanism attributed the genotoxicity to the binding to the DNA of the end product of the chromium(III) reduction.

Chromium salts (chromates) are also the cause of allergic reactions in some people. Chromates are often used to manufacture, amongst other things, leather products, paints, cement, mortar and anti-corrosives. Contact with products containing chromates can lead to allergic contact dermatitis and irritant dermatitis, resulting in ulceration of the skin, sometimes referred to as "chrome ulcers". This condition is often found in workers that have been exposed to strong chromate solutions in electroplating, tanning and chrome-producing manufacturers.

Environmental issues

As chromium compounds were used in dyes and paints and the tanning of leather, these compounds are often found in soil and groundwater at abandoned industrial sites, now needing environmental cleanup and remediation per the treatment of brownfield land. Primer paint containing hexavalent chromium is still widely used for aerospace and automobile refinishing applications.

In 2010, the Environmental Working Group studied the drinking water in 35 American cities. The study was the first nationwide analysis measuring the presence of the chemical in U.S. water systems. The study found measurable hexavalent chromium in the tap water of 31 of the cities sampled, with Norman, Oklahoma, at the top of list; 25 cities had levels that exceeded California's proposed limit. Note: Concentrations of Cr(VI) in US municipal drinking water supplies reported by EWG are within likely, natural background levels for the areas tested and not necessarily indicative of industrial pollution (CalEPA Fact Sheet), as asserted by EWG. This factor was not taken into consideration in their report.