Beryllium

Beryllium
4Be
- ↑ Be ↓ Mg Periodic table lithium ← beryllium → boron
Appearance
white-gray metallic
General properties
Name, symbol, number	beryllium, Be, 4
Pronunciation	/ b ə ˈ r ɪ l i ə m / bə-RIL-ee-əm
Metallic category	alkaline earth metal
Group, period, block	2 (alkaline earth metals), 2, s
Standard atomic weight	9.012182(3)
Electron configuration	[He] 2s2 2, 2
History
Discovery	Louis Nicolas Vauquelin (1797)
First isolation	Friedrich Wöhler & Antoine Bussy (1828)
Physical properties
Phase	solid
Density (near r.t.)	1.85 g·cm−3
Liquid density at m.p.	1.690 g·cm−3
Melting point	1560 K, 1287 °C, 2349 °F
Boiling point	2742 K, 2469 °C, 4476 °F
Heat of fusion	12.2 kJ·mol−1
Heat of vaporization	297 kJ·mol−1
Molar heat capacity	16.443 J·mol−1·K−1
Vapor pressure
P (Pa) 1 10 100 1 k 10 k 100 k at T (K) 1462 1608 1791 2023 2327 2742
Atomic properties
Oxidation states	2, 1 ( amphoteric oxide)
Electronegativity	1.57 (Pauling scale)
Ionization energies ( more)	1st: 899.5 kJ·mol−1
	2nd: 1757.1 kJ·mol−1
	3rd: 14848.7 kJ·mol−1
Atomic radius	112 pm
Covalent radius	96±3 pm
Van der Waals radius	153 pm
Miscellanea
Crystal structure	hexagonal close-packed
Magnetic ordering	diamagnetic
Electrical resistivity	(20 °C) 36 nΩ·m
Thermal conductivity	200 W·m−1·K−1
Thermal expansion	(25 °C) 11.3 µm·m−1·K−1
Speed of sound (thin rod)	( r.t.) 12870 m·s−1
Young's modulus	287 GPa
Shear modulus	132 GPa
Bulk modulus	130 GPa
Poisson ratio	0.032
Mohs hardness	5.5
Vickers hardness	1670 MPa
Brinell hardness	600 MPa
CAS registry number	7440-41-7
Most stable isotopes
Main article: Isotopes of beryllium
iso NA half-life DM DE ( MeV) DP 7Be trace 53.12 d ε 0.862 7Li γ 0.477 - 9Be 100% 9Be is stable with 5 neutrons 10Be trace 1.36×106 y β− 0.556 10B

Beryllium is the chemical element with the symbol Be and atomic number 4. Because any beryllium synthesized in stars is short-lived, it is a relatively rare element in both the universe and in the crust of the Earth. It is a divalent element which occurs naturally only in combination with other elements in minerals. Notable gemstones which contain beryllium include beryl ( aquamarine, emerald) and chrysoberyl. As a free element it is a steel-gray, strong, lightweight and brittle alkaline earth metal.

Beryllium increases hardness and resistance to corrosion when alloyed to aluminium, cobalt, copper (notably beryllium copper), iron and nickel. In structural applications, high flexural rigidity, thermal stability, thermal conductivity and low density (1.85 times that of water) make beryllium a quality aerospace material for high-speed aircraft, missiles, space vehicles and communication satellites. Because of its low density and atomic mass, beryllium is relatively transparent to X-rays and other forms of ionizing radiation; therefore, it is the most common window material for X-ray equipment and in particle physics experiments. The high thermal conductivities of beryllium and beryllium oxide have led to their use in heat transport and heat sinking applications.

The commercial use of beryllium metal presents technical challenges due to the toxicity (especially by inhalation) of beryllium-containing dusts. Beryllium is corrosive to tissue, and can cause a chronic life-threatening allergic disease called berylliosis in some people. The element is not known to be necessary or useful for either plant or animal life.

Characteristics

Physical properties

Beryllium is a steel gray and hard metal that is brittle at room temperature and has a close-packed hexagonal crystal structure. It has exceptional flexural rigidity ( Young's modulus 287 GPa) and a reasonably high melting point. The modulus of elasticity of beryllium is approximately 50% greater than that of steel. The combination of this modulus and a relatively low density results in an unusually fast sound conduction speed in beryllium – about 12.9 km/s at ambient conditions. Other significant properties are high specific heat (1925 J·kg⁻¹·K⁻¹) and thermal conductivity (216 W·m⁻¹·K⁻¹), which make beryllium the metal with the best heat dissipation characteristics per unit weight. In combination with the relatively low coefficient of linear thermal expansion (11.4×10⁻⁶ K⁻¹), these characteristics result in a unique stability under conditions of thermal loading.

Nuclear properties

Natural beryllium, save for slight contamination by cosmogenic radioisotopes, is essentially beryllium-9, which has a nuclear spin of 3/2-. Beryllium has a large scattering cross section for high-energy neutrons, about 6 barns for energies above ~0.01 MeV. Therefore, it works as a neutron reflector and neutron moderator, effectively slowing the neutrons to the thermal energy range of below 0.03 eV, where the total cross section is at least an order of magnitude lower – exact value strongly depends on the purity and size of the crystallites in the material.

The single primordial beryllium isotope ⁹Be also undergoes a (n,2n) neutron reaction with neutron energies over about 1.9 MeV, to produce ⁸Be, which almost immediately breaks into two alpha particles. Thus, for high-energy neutrons beryllium is a neutron multiplier, releasing more neutrons than it absorbs. This nuclear reaction is:

9
4Be + n → 2(4
2He) + 2n

Neutrons are liberated when beryllium nuclei are struck by energetic alpha particles producing the nuclear reaction

9
4Be + 4
2He → 12
6C + n , where 4
2He is an alpha particle and 12
6C is a carbon-12 nucleus.

Beryllium also releases neutrons under bombardment by gamma rays. Thus, natural beryllium bombarded either by alphas or gammas from a suitable radioisotope is a key component of most radioisotope-powered nuclear reaction neutron sources for the laboratory production of free neutrons.

As a metal, beryllium is transparent to most wavelengths of X-rays and gamma rays, making it useful for the output windows of X-ray tubes and other such apparatus.

Isotopes and nucleosynthesis

Both stable and unstable isotopes of beryllium are created in stars, but these do not last long. It is believed that most of the stable beryllium in the universe was originally created in the interstellar medium when cosmic rays induced fission in heavier elements found in interstellar gas and dust. Primordial beryllium contains only one stable isotope, ⁹Be, and therefore beryllium is a monoisotopic element.

Radioactive cosmogenic ¹⁰Be is produced in the atmosphere of the Earth by the cosmic ray spallation of oxygen. ¹⁰Be accumulates at the soil surface, where its relatively long half-life (1.36 million years) permits a long residence time before decaying to boron-10. Thus, ¹⁰Be and its daughter products are used to examine natural soil erosion, soil formation and the development of lateritic soils, and as a proxy for measurement of the variations in solar activity and the age of ice cores. The production of ¹⁰Be is inversely proportional to solar activity, because increased solar wind during periods of high solar activity decreases the flux of galactic cosmic rays that reach the Earth. Nuclear explosions also form ¹⁰Be by the reaction of fast neutrons with ¹³C in the carbon dioxide in air. This is one of the indicators of past activity at nuclear weapon test sites. The isotope ⁷Be (half-life 53 days) is also cosmogenic, and shows an atmospheric abundance linked to sunspots, much like ¹⁰Be.

⁸Be has a very short half-life of about 7×10⁻¹⁷ s that contributes to its significant cosmological role, as elements heavier than beryllium could not have been produced by nuclear fusion in the Big Bang. This is due to the lack of sufficient time during the Big Bang's nucleosynthesis phase to produce carbon by the fusion of ⁴He nuclei and the very low concentrations of available beryllium-8. The British astronomer Sir Fred Hoyle first showed that the energy levels of ⁸Be and ¹²C allow carbon production by the so-called triple-alpha process in helium-fueled stars where more nucleosynthesis time is available. This process allows carbon to be produced in stars, but not in the Big Bang. Star-created carbon (the basis of carbon-based life) is thus a component in the elements in the gas and dust ejected by AGB stars and supernovae (see also Big Bang nucleosynthesis), as well as the creation of all other elements with atomic numbers larger than that of carbon.

The innermost electrons of beryllium may contribute to chemical bonding. Therefore, when ⁷Be decays by electron capture, it does so by taking electrons from atomic orbitals that may participate in bonding. This makes its decay rate dependent to a measurable degree upon its electron configuration – a rare occurrence in nuclear decay.

The shortest-lived known isotope of beryllium is ¹³Be which decays through neutron emission. It has a half-life of 2.7 × 10⁻²¹ s. ⁶Be is also very short-lived with a half-life of 5.0 × 10⁻²¹ s. The exotic isotopes ¹¹Be and ¹⁴Be are known to exhibit a nuclear halo. This phenomenon can be understood as the nuclei of ¹¹Be and ¹⁴Be have, respectively, 1 and 4 neutrons orbiting substantially outside the classical Fermi 'waterdrop' model of the nucleus.

Occurrence

Beryllium has a concentration of 2 to 6 parts per million (ppm) in the Earth's crust. The Sun has a concentration of 0.1 parts per billion (ppb) of beryllium, similar to that of rhenium. It is most concentrated in the soils, 6 ppm, and is found in 0.2 parts per trillion (ppt) of sea water. Trace amounts of ⁹Be are found in the Earth's atmosphere. In sea water, beryllium is exceedingly rare, more so than even scandium, comprising only 0.0006 ppb by weight. In stream water, however, beryllium is more abundant with 0.1 ppb by weight.

Beryllium is found in over 100 minerals, but most are uncommon to rare. The more common beryllium containing minerals include: bertrandite (Be₄Si₂O₇(OH)₂), beryl (Al₂Be₃Si₆O₁₈), chrysoberyl (Al₂BeO₄) and phenakite (Be₂SiO₄). Precious forms of beryl are aquamarine, bixbite and emerald. The green colour in gem-quality forms of beryl comes from varying amounts of chromium (about 2% for emerald).

The two main ores of beryllium, beryl and bertrandite, are found in Argentina, Brazil, India, Madagascar, Russia and the United States. Total world reserves of beryllium ore are greater than 400,000 tonnes.

Production

The extraction of beryllium from its compounds is a difficult process due to its high affinity for oxygen at elevated temperatures, and its ability to reduce water when its oxide film is removed. The United States, China and Kazakhstan are the only three countries involved in the industrial scale extraction of beryllium.

Beryllium is most-commonly extracted from beryl, which is either sintered using an extraction agent or melted into a soluble mixture. The sintering process involves mixing beryl with sodium fluorosilicate and soda at 770°C to form sodium fluoroberyllate, aluminium oxide and silicon dioxide. Beryllium hydroxide is precipitated from a solution of sodium fluoroberyllate and sodium hydroxide in water. Extraction of beryllium using the melt method involves grinding beryl into a powder and heating it to 1650°C. The melt is quickly cooled with water and then reheated 250 to 300°C in concentrated sulfuric acid, mostly yielding beryllium sulfate and aluminium sulfate. Aqueous ammonia is then used to remove the aluminium and sulfur, leaving beryllium hydroxide.

Beryllium hydroxide created using either the sinter or melt method is then converted into beryllium fluoride or beryllium chloride. To form the fluoride, aqueous ammonium hydrogen fluoride is added to beryllium hydroxide to yield a precipitate of ammonium tetrafluoroberyllate, which is heated to 1000°C to form beryllium fluoride. Heating the fluoride to 900°C with magnesium forms finely divided beryllium and additional heating to 1300°C creates the compact metal. Heating beryllium hydroxide forms the oxide which becomes beryllium chloride when mixed with carbon and chloride. Electrolysis of molten beryllium chloride is then used to obtain the metal.

Chemical properties

Beryllium's chemical behaviour is largely a result of its small atomic and ionic radii. It thus has very high ionization potentials and strong polarization while bonded to other atoms, which is why all of its compounds are covalent. It is more chemically similar to aluminium than its close neighbors in the periodic table due to having a similar charge-to-radius ratio. An oxide layer forms around beryllium that prevents further reactions with air unless heated above 1000°C. Once ignited, beryllium burns brilliantly forming a mixture of beryllium oxide and beryllium nitride. Beryllium dissolves readily in non- oxidizing acids, such as HCl and diluted H₂SO₄, but not in nitric acid or water as this forms the oxide. This behaviour is similar to that of aluminium metal. Beryllium also dissolves in alkali solutions.

The beryllium atom has the electronic configuration [He] 2s². The two valence electrons give beryllium a +2 oxidation state and the thus the ability to form two covalent bonds; the only evidence of lower valence of beryllium is in the solubility of the metal in BeCl₂. Due to the octet rule, atoms tend to seek a valence of 8 in order to resemble a noble gas. Beryllium tries to achieve a coordination number of 4 because its two covalent bonds fill half of this octet. A coordination of 4 allows beryllium compounds, such as the fluoride or chloride, to form polymers.

This characteristic is employed in analytical techniques using EDTA as a ligand. EDTA preferentially forms octahedral complexes – thus absorbing other cations such as Al³⁺ which might interfere – for example, in the solvent extraction of a complex formed between Be²⁺ and acetylacetone. Beryllium(II) readily forms complexes with strong donating ligands such as phosphine oxides and arsine oxides. There have been extensive studies of these complexes which show the stability of the O-Be bond.

Solutions of beryllium salts, e.g. beryllium sulfate and beryllium nitrate, are acidic because of hydrolysis of the [Be(H₂O)₄]²⁺ ion.

[Be(H₂O)₄]²⁺ + H₂O [Be(H₂O)₃(OH)]⁺ + H₃O⁺

Other products of hydrolysis include the trimeric ion [Be₃(OH)₃(H₂O)₆]³⁺. Beryllium hydroxide, Be(OH)₂, is insoluble even in acidic solutions with pH less than 6, that is at biological pH. It is amphoteric and dissolves in strongly alkaline solutions.

Beryllium forms binary compounds with many non-metals. Anhydrous halides are known for F, Cl, Br and I. BeF₂ has a silica-like structure with corner-shared BeF₄ tetrahedra. BeCl₂ and BeBr₂ have chain structures with edge-shared tetrahedra. All beryllium halides have a linear monomeric molecular structure in the gas phase.

Beryllium difluoride, BeF₂, is different than the other difluorides. In general, beryllium has a tendency to bond covalently, much more so than the other alkaline earths and its fluoride is partially covalent (although still more ionic than its other halides). BeF₂ has many similarities to SiO₂ (quartz) a mostly covalently bonded network solid. BeF₂ has tetrahedrally coordinated metal and forms glasses (is difficult to crystallize). When crystalline, beryllium fluoride has the same room temperature crystal structure as quartz and shares many higher temperatures structures also. Beryllium difluoride is very soluble in water, unlike the other alkaline earths. (Although they are strongly ionic, they do not dissolve because of the especially strong lattice energy of the fluorite structure.) However, BeF₂ has much lower electrical conductivity when in solution or when molten than would be expected if it were fully ionic.

Order and disorder in difluorides
The strong and stable ionic fluorite structure adopted by calcium difluoride and many other difluorides	Disordered structure of beryllium glass (sketch, two dimensions)

Beryllium oxide, BeO, is a white refractory solid, which has the wurtzite crystal structure and a thermal conductivity as high as in some metals. BeO is amphoteric. Salts of beryllium can be produced by treating Be(OH)₂ with acid. Beryllium sulfide, selenide and telluride are known, all having the zincblende structure.

Beryllium nitride, Be₃N₂ is a high-melting-point compound which is readily hydrolyzed. Beryllium azide, BeN₆ is known and beryllium phosphide, Be₃P₂ has a similar structure to Be₃N₂. Basic beryllium nitrate and basic beryllium acetate have similar tetrahedral structures with four beryllium atoms coordinated to a central oxide ion. A number of beryllium borides are known, such as Be₅B, Be₄B, Be₂B, BeB₂, BeB₆ and BeB₁₂. Beryllium carbide, Be₂C, is a refractory brick-red compound that reacts with water to give methane. No beryllium silicide has been identified.

History

The mineral beryl, which contains beryllium, has been used at least since the Ptolemaic dynasty of Egypt. In the first century CE, Roman naturalist Pliny the Elder mentioned in his encyclopedia Natural History that beryl and emerald ("smaragdus") were similar. The Papyrus Graecus Holmiensis, written in the third or fourth century CE, contains notes on how to prepare artificial emerald and beryl.

Early analyses of emeralds and beryls by Martin Heinrich Klaproth, Torbern Olof Bergman, Franz Karl Achard, and Johann Jakob Bindheim always yielded similar elements, leading to the fallacious conclusion that both substances are aluminium silicates. Mineralogist René Just Haüy discovered that both crystals are geometrically identical, and he asked chemist Louis-Nicolas Vauquelin for a chemical analysis.

In a 1797 paper read before the Annales de chimie et de physique, Vauquelin reported that he found a new "earth" by dissolving aluminium hydroxide from emerald and beryl in an additional alkali. Vauquelin named the new earth "glucina" for the sweet taste of some of its compounds. Klaproth preferred the name "beryllia" due to fact that yttria also formed sweet salts.

Friedrich Wöhler and Antoine Bussy independently isolated beryllium in 1828 by the chemical reaction of metallic potassium with beryllium chloride, as follows:

BeCl₂ + 2 K → 2 KCl + Be

Using an alcohol lamp, Wöhler heated alternating layers of beryllium chloride and potassium in a wired-shut platinum crucible. The above reaction immediately took place and caused the crucible to become white hot. Upon cooling and washing the resulting gray-black powder he saw that it was made of fine particles with a dark metallic luster. The highly reactive potassium had been produced by the electrolysis of its compounds, a process discovered 21 years before. The chemical method using potassium yielded only small grains of beryllium from which no ingot of metal could be cast or hammered.

The direct electrolysis of a molten mixture of beryllium fluoride and sodium fluoride by Paul Lebeau in 1898 resulted in the first pure (99.5 to 99.8%) samples of beryllium. The first commercially-successful process for producing beryllium was developed in 1932 by Alfred Stock and Hans Goldschmidt. Their process involves the electrolysation of a mixture of beryllium fluorides and barium, which causes molten beryllium to collect on a water-cooled iron cathode.

A sample of beryllium was bombarded with alpha rays from the decay of radium in a 1932 experiment by James Chadwick that uncovered the existence of the neutron. This same method is used in one class of radioisotope-based laboratory neutron sources that produce 30 neutrons for every million α particles.

Beryllium production saw a rapid increase during World War II, due to the rising demand for hard beryllium-copper alloys and phosphors for fluorescent lights. Most early fluorescent lamps used zinc orthosilicate with varying content of beryllium to emit greenish light. Small additions of magnesium tungstate improved the blue part of the spectrum to yield an acceptable white light. Halophosphate-based phosphors replaced beryllium-based phosphors after beryllium was found to be toxic.

Electrolysis of a mixture of beryllium fluoride and sodium fluoride was used to isolate beryllium during the 19th century. The metal's high melting point makes this process more energy-consuming than corresponding processes used for the alkali metals. Early in the 20th century, the production of beryllium by the thermal decomposition of beryllium iodide was investigated following the success of a similar process for the production of zirconium, but this process proved to be uneconomical for volume production.

Pure beryllium metal did not become readily available until 1957, even though it had been used as an alloying metal to harden and toughen copper much earlier. Beryllium could be produced by reducing beryllium compounds such as beryllium chloride with metallic potassium or sodium. Currently most beryllium is produced by reducing beryllium fluoride with purified magnesium. The price on the American market for vacuum-cast beryllium ingots was about $338 per pound ($745 per kilogram) in 2001.

Between 1998 and 2008, the world's production of beryllium had decreased from 343 to about 200 tonnes, of which 176 tonnes (88%) came from the United States.

Etymology

Early usage of the word beryllium can be traced to many languages, including Latin Beryllus; French Béry; Greek βήρυλλος, bērullos, beryl; Prakrit veruliya (वॆरुलिय‌); Pāli veḷuriya (वेलुरिय), veḷiru (भेलिरु) or viḷar (भिलर्) – "to become pale", in reference to the pale semiprecious gemstone beryl. The original source is probably the Sanskrit word वैडूर्य vaidurya-, which is of Dravidian origin and could be derived from the name of the modern city of Belur. For about 160 years, beryllium was also known as glucinum or glucinium (with the accompanying chemical symbol "Gl",), the name coming from the Greek word for sweet: γλυκυς, due to the sweet taste of beryllium salts.

Applications

It is estimated that most beryllium is used for military applications, so information is not readily available.

Radiation windows

Because of its low atomic number and very low absorption for X-rays, the oldest and still one of the most important applications of beryllium is in radiation windows for X-ray tubes. Extreme demands are placed on purity and cleanliness of beryllium to avoid artifacts in the X-ray images. Thin beryllium foils are used as radiation windows for X-ray detectors, and the extremely low absorption minimizes the heating effects caused by high intensity, low energy X-rays typical of synchrotron radiation. Vacuum-tight windows and beam-tubes for radiation experiments on synchrotrons are manufactured exclusively from beryllium. In scientific setups for various X-ray emission studies (e.g., energy-dispersive X-ray spectroscopy) the sample holder is usually made of beryllium because its emitted X-rays have much lower energies (~100 eV) than X-rays from most studied materials.

Low atomic number also makes beryllium relatively transparent to energetic particles. Therefore it is used to build the beam pipe around the collision region in particle physics setups, such as all four main detector experiments at the Large Hadron Collider ( ALICE, ATLAS, CMS, LHCb), the Tevatron and the SLAC. The low density of beryllium allows collision products to reach the surrounding detectors without significant interaction, its stiffness allows a powerful vacuum to be produced within the pipe to minimize interaction with gases, its thermal stability allows it to function correctly at temperatures of only a few degrees above absolute zero, and its diamagnetic nature keeps it from interfering with the complex multipole magnet systems used to steer and focus the particle beams.

Mechanical applications

Because of its stiffness, light weight and dimensional stability over a wide temperature range, beryllium metal is used for lightweight structural components in the defense and aerospace industries in high-speed aircraft, guided missiles, space vehicles, and satellites. Several liquid-fuel rockets have used rocket nozzles made of pure beryllium. Beryllium powder was itself studied as a rocket fuel, but this use has never materialized. A small number of bicycle frames were built with beryllium, at "astonishing" prices. From 1998 to 2000, the McLaren Formula One team used Mercedes-Benz engines with beryllium-aluminium- alloy pistons. The use of beryllium engine components was banned following a protest by Scuderia Ferrari.

Mixing about 2.0% beryllium into copper forms an alloy called beryllium copper that is six times stronger than copper alone. Beryllium alloys are used in many applications because of their combination of elasticity, high electrical conductivity and thermal conductivity, high strength and hardness, nonmagnetic properties, as well as its good corrosion and fatigue resistance. These applications include non-sparking tools that are used near flammable gases ( beryllium nickel), in springs and membranes (beryllium nickel and beryllium iron) used in surgical instruments and high temperature devices. As little as 50 parts per million of beryllium alloyed with liquid magnesium leads to a significant increase in oxidation resistance and decrease in flammability.

The excellent elastic rigidity of beryllium has led to its extensive use in precision instrumentation, e.g. in inertial guidance systems and in the support mechanisms for optical systems. Beryllium-copper alloys were also applied as a hardening agent in "Jason pistols", which were used to strip the paint from the hulls of ships.

An earlier major application of beryllium was in brakes for military airplanes because of its hardness, high melting point, and exceptional ability to dissipate heat. Environmental considerations have led to substitution by other materials.

To reduce costs, beryllium can be alloyed with significant amounts of aluminium, resulting in the AlBeMet alloy (a trade name). This blend is cheaper than pure beryllium, while still retaining many desirable properties.

Mirrors

Beryllium mirrors are of particular interest. Large-area mirrors, frequently with a honeycomb support structure, are used, for example, in meteorological satellites where low weight and long-term dimensional stability are critical. Smaller beryllium mirrors are used in optical guidance systems and in fire-control systems, e.g. in the German-made Leopard 1 and Leopard 2 main battle tanks. In these systems, very rapid movement of the mirror is required which again dictates low mass and high rigidity. Usually the beryllium mirror is coated with hard electroless nickel plating which can be more easily polished to a finer optical finish than beryllium. In some applications, though, the beryllium blank is polished without any coating. This is particularly applicable to cryogenic operation where thermal expansion mismatch can cause the coating to buckle.

The James Webb Space Telescope will have 18 hexagonal beryllium sections for its mirrors. Because JWST will face a temperature of 33 K, the mirror is made of beryllium, capable of handling extreme cold better than glass. Beryllium contracts and deforms less than glass – and remains more uniform – in such temperatures. For the same reason, the optics of the Spitzer Space Telescope are entirely built of beryllium metal.

Magnetic applications

Beryllium is non-magnetic. Therefore, tools fabricated out of beryllium are used by naval or military explosive ordnance disposal teams for work on or near naval mines, since these mines commonly have magnetic fuzes. They are also found in maintenance and construction materials near magnetic resonance imaging (MRI) machines because of the high magnetic fields generated by them. In the fields of radio communications and powerful (usually military) radars, hand tools made of beryllium are used to tune the highly magnetic klystrons, magnetrons, traveling wave tubes, etc., that are used for generating high levels of microwave power in the transmitters.

Nuclear applications

Thin plates or foils of beryllium are sometimes used in nuclear weapon designs as the very outer layer of the plutonium pits in the primary stages of thermonuclear bombs, placed to surround the fissile material. These layers of beryllium are good "pushers" for the implosion of the plutonium-239, and they are also good neutron reflectors, just as they are in beryllium-moderated nuclear reactors.

Beryllium is also commonly used in some neutron sources in laboratory devices in which relatively few neutrons are needed (rather than having to use a nuclear reactor, or an particle accelerator-powered neutron generator). For this purpose, a target of beryllium-9 is bombarded with energetic alpha particles from a radioisotope such as polonium-210, radium-226, plutonium-239, or americium-241. In the nuclear reaction that occurs, a beryllium nucleus is transmuted into carbon-12, and one free neutron is emitted, traveling in about the same direction as the alpha particle was heading. Such alpha decay driven beryllium neutron sources, named "urchin" neutron initiators, were used some in early atomic bombs. Neutron sources in which beryllium is bombarded with gamma rays from a gamma decay radioisotope, are also used to produce laboratory neutrons.

Beryllium is also used at the Joint European Torus nuclear-fusion research laboratory, and it will be used in the more advanced ITER to condition the components which face the plasma. Beryllium has also been proposed as a cladding material for nuclear fuel rods, because of its good combination of mechanical, chemical, and nuclear properties. Beryllium fluoride is one of the constituent salts of the eutectic salt mixture FLiBe, which is used as a solvent, moderator and coolant in many hypothetical molten salt reactor designs.

Acoustics

Low weight and high rigidity of beryllium make it useful as a material for high-frequency speaker drivers. Because beryllium is expensive (many times more than titanium), hard to shape due to its brittleness, and toxic if mishandled, beryllium tweeters are limited to high-end home, pro audio, and public address applications. Due to the high performance of beryllium in acoustics, for marketing purposes some products are claimed to be made of the material when they are not.

Electronic

Beryllium is a p-type dopant in III-V compound semiconductors. It is widely used in materials such as GaAs, AlGaAs, InGaAs and InAlAs grown by molecular beam epitaxy (MBE). Cross-rolled beryllium sheet is an excellent structural support for printed circuit boards in surface-mount technology. In critical electronic applications, beryllium is both a structural support and heat sink. The application also requires a coefficient of thermal expansion that is well matched to the alumina and polyimide-glass substrates. The beryllium-beryllium oxide composite " E-Materials" have been specially designed for these electronic applications and have the additional advantage that the thermal expansion coefficient can be tailored to match diverse substrate materials.

Beryllium oxide is useful for many applications that require the combined properties of an electrical insulator and an excellent heat conductor, with high strength and hardness, and a very high melting point. Beryllium oxide is frequently used as an insulator base plate in high-power transistors in radio frequency transmitters for telecommunications. Beryllium oxide is also being studied for use in increasing the thermal conductivity of uranium dioxide nuclear fuel pellets. Beryllium compounds were used in fluorescent lighting tubes, but this use was discontinued because of the disease berylliosis which developed in the workers who were making the tubes.

Precautions

Approximately 35 micrograms of beryllium is found in the human body, but this amount is not considered harmful. Beryllium is chemically similar to magnesium and therefore can displace it from enzymes, which causes them to malfunction. Chronic berylliosis is a pulmonary and systemic granulomatous disease caused by inhalation of dust or fumes contaminated with beryllium; either large amounts over a short time or small amounts over a long time can lead to this ailment. Symptoms of the disease can take up to 5 years to develop; about a third of patients with it die and the survivors are left disabled. The International Agency for Research on Cancer (IARC) lists beryllium and beryllium compounds as Category 1 carcinogens.

Acute beryllium disease in the form of chemical pneumonitis was first reported in Europe in 1933 and in the United States in 1943. A survey found that about 5% of workers in plants manufacturing fluorescent lamps in 1949 in the United States had beryllium-related lung diseases. Chronic berylliosis resembles sarcoidosis in many respects, and the differential diagnosis is often difficult. It killed some early workers in nuclear weapons design, such as Herbert L. Anderson.

Early researchers tasted beryllium and its various compounds for sweetness in order to verify its presence. Modern diagnostic equipment no longer necessitates this highly risky procedure and no attempt should be made to ingest this highly toxic substance. Beryllium and its compounds should be handled with great care and special precautions must be taken when carrying out any activity which could result in the release of beryllium dust (lung cancer is a possible result of prolonged exposure to beryllium laden dust). Although the use of beryllium compounds in fluorescent lighting tubes was discontinued in 1949, potential for exposure to beryllium exists in the nuclear and aerospace industries and in the refining of beryllium metal and melting of beryllium-containing alloys, the manufacturing of electronic devices, and the handling of other beryllium-containing material.

A successful test for beryllium in air and on surfaces has been recently developed and published as an international voluntary consensus standard ASTM D7202. The procedure uses dilute ammonium bifluoride for dissolution and fluorescence detection with beryllium bound to sulfonated hydroxybenzoquinoline, allowing up to 100 times more sensitive detection than the recommended limit for beryllium concentration in the workplace. Fluorescence increases with increasing beryllium concentration. The new procedure has been successfully tested on a variety of surfaces and is effective for the dissolution and ultratrace detection of refractory beryllium oxide and siliceous beryllium (ASTM D7458).